From: Characterizations and Quantitative Estimation of Alkali-Activated Binder Paste from Microstructures
Mix | Age (days) | v f,AAB + v f,CSH(S) | ||
---|---|---|---|---|
23 °C | 40 °C | 60 °C | ||
FA 100 | 7 | 0.133 | 0.133 | 0.333 |
28 | 0.267 | 0.300 | 0.400 | |
90 | 0.433 | 0.500 | 0.533 | |
FA 85 SG 15 | 7 | 0.178 | 0.178 | 0.323 |
28 | 0.301 | 0.311 | 0.422 | |
90 | 0.467 | 0.511 | 0.555 | |
FA 70 SG 30 | 7 | 0.211 | 0.211 | 0.322 |
28 | 0.332 | 0.345 | 0.433 | |
90 | 0.500 | 0.533 | 0.567 | |
FA 50 SG 50 | 7 | 0.245 | 0.256 | 0.323 |
28 | 0.355 | 0.355 | 0.422 | |
90 | 0.533 | 0.555 | 0.588 | |
FA 30 SG 70 | 7 | 0.266 | 0.277 | 0.322 |
28 | 0.389 | 0.400 | 0.433 | |
90 | 0.567 | 0.588 | 0.589 | |
FA 15 SG 85 | 7 | 0.295 | 0.300 | 0.322 |
28 | 0.422 | 0.411 | 0.423 | |
90 | 0.589 | 0.589 | 0.600 | |
SG 100 | 7 | 0.322 | 0.322 | 0.322 |
28 | 0.422 | 0.433 | 0.433 | |
90 | 0.600 | 0.600 | 0.600 | |
FA 100 p15 | 7 | 0.133 | 0.133 | 0.333 |
28 | 0.267 | 0.300 | 0.400 | |
90 | 0.433 | 0.500 | 0.533 | |
FA 100 p30 | 7 | 0.133 | 0.133 | 0.333 |
28 | 0.267 | 0.300 | 0.400 | |
90 | 0.433 | 0.500 | 0.533 | |
FA 100 p60 | 7 | 0.133 | 0.133 | 0.333 |
28 | 0.267 | 0.300 | 0.400 | |
90 | 0.433 | 0.500 | 0.533 |