(a/w) | Current study | Sherbini (2014) | |||||||
---|---|---|---|---|---|---|---|---|---|
S/PP | S/G | G/PP | S/G/PP | S | G | PP | |||
Mode II fracture toughness (Mean ± SD) K IIC MPa√mm | DENP | 0.3 | 75 ± 2.91 | 73 ± 2.10 | 70 ± 3.48 | 66 ± 1.54 | 65 | 66.4 | 69.6 |
0.4 | 70 ± 2.00 | 67 ± 3.11 | 65 ± 1.72 | 62 ± 2.65 | 60 | 61.1 | 66.4 | ||
0.5 | 69 ± 3.21 | 65 ± 1.58 | 63 ± 2.02 | 58 ± 1.19 | 56.9 | 60.1 | 66.4 | ||
DNC | 0.3 | 143 ± 4.72 | 137 ± 4.45 | 105 ± 4.79 | 100 ± 4.89 | 135 | 111 | 123 | |
0.4 | 129 ± 5.16 | 126 ± 4.63 | 96 ± 3.78 | 95 ± 2.45 | 122 | 105 | 110 | ||
0.5 | 118 ± 5.88 | 117 ± 5.50 | 95 ± 3.30 | 95 ± 4.57 | 107 | 103 | 106 | ||
BND | 0.3 | 45.5 ± 1.68 | 43 ± 1.02 | 44 ± 2.02 | 37.5 ± 0.78 | 40.6 | 36.4 | 41.5 | |
0.4 | 42 ± 1.69 | 40 ± 1.57 | 41 ± 1.14 | 34.5 ± 0.99 | 36.7 | 35 | 39 | ||
0.5 | 41 ± 1.89 | 39 ± 1.13 | 41 ± 1.73 | 34 ± 1.57 | 36.1 | 34.8 | 37 | ||
4PS | 0.3 | 40 ± 1.97 | 38 ± 1.66 | 27 ± 0.84 | 28 ± 0.58 | 37 | 33.5 | 36 | |
0.4 | 35 ± 1.62 | 34 ± 1.48 | 25 ± 0.72 | 26 ± 1.13 | 32.5 | 29.2 | 30.7 | ||
0.5 | 34 ± 1.02 | 32 ± 0.99 | 25 ± 0.72 | 25.5 ± 0.76 | 31 | 27.4 | 30 |