References | Fiber (L/D) (mm/mm) | Fiber content (%) | Specimen size (mm) | Flexural strength (MPa) |
---|---|---|---|---|
Collepardi et al. (1997) | 13/0.18 | 2.5 | 150 × 150 × 600 | 20.2 |
40 × 40 × 160 | 48.3 | |||
Herold and Muller (2004) | 8/0.17 | 0.0 | 40 × 40 × 160 | 21.1 |
0.5 | 25.3 | |||
2.5 | 34.1 | |||
4.0 | 46.2 | |||
Bornemann and Faber (2004) | 9/0.15 | 2.0 | 150 × 150 × 700 | 22.0 |
Guvensoy et al. (2004) | 6/0.15 | 5.0 | 70 × 70 × 280 | 30.3 |
5.5 | 49.2 | |||
6.0 | 54.4 | |||
Orgass and Klug (2004) | 13/0.16 | 0.0 | 150 × 150 × 700 | 10.6 |
1.0 | 11.9 | |||
2.0 | 13.4 | |||
0.0 | 100 × 100 × 500 | 9.8 | ||
1.0 | 11.2 | |||
2.0 | 14.7 | |||
0.0 | 40 × 40 × 160 | 9.9 | ||
1.0 | 11.6 | |||
2.0 | 18.3 | |||
Soutsos et al. (2005) | 12/0.16 | 0.0 | 40 × 40 × 160 | 18.4 |
1.5 | 37.3 | |||
2.0 | 40.3 | |||
Allena and Newtson (2010) | 13/– | 0.0 | 75 × 100 × 400 | 10.9 |
1.5 | 18.3 | |||
Wille and Parra-Montesinos (2012) | 13/0.20 | 1.5 | 152 × 152 × 508 | 14.8 |
102 × 102 × 406 | 15.8 | |||
Magureanu et al. (2012) | 25/0.40 + 6/0.17 | 0.0 | 40 × 40 × 160 | 13.9 |
2.5 | 34.0 | |||
0.0 | 100 × 100 × 300 | 9.4 | ||
2.5 | 23.0 | |||
Kazemi and Lubell (2012) | 13/0.2 | 0.0 | 50 × 50 × 150 | 22.1 |
2.0 | 29.1 | |||
4.0 | 48.0 | |||
0.0 | 100 × 100 × 300 | 15.0 | ||
2.0 | 23.1 | |||
4.0 | 38.4 | |||
Kreiger et al. (2012) | 14/0.18 | 2.0 | 51 × 51 × 229 | 18.4 |
51 × 51 × 343 | 19.8 | |||
51 × 51 × 457 | 17.5 | |||
51 × 51 × 699 | 18.0 | |||
76 × 76 × 343 | 19.0 | |||
Shu-hua et al. (2012) | 18/0.20 | 0.0 | 40 × 40 × 160 | 26.9 |
1.0 | 27.6 | |||
2.0 | 29.2 | |||
0.0 | 100 × 100 × 400 | 17.7 | ||
1.0 | 18.9 | |||
2.0 | 20.0 | |||
Nguyen et al. (2013) | (30/0.3 twisted) + (13/0.2 smooth) | 1.0 + 0.5 | 50 × 50 × 150 | 29.6 |
1.0Â +Â 1.0 | 38.9 | |||
1.0 + 0.5 | 100 × 100 × 300 | 23.9 | ||
1.0Â +Â 1.0 | 29.1 | |||
1.0 + 0.5 | 150 × 150 × 450 | 20.5 | ||
1.0Â +Â 1.0 | 26.9 |