From: Assessment of Rheological and Piezoresistive Properties of Graphene based Cement Composites
Sample | Flow diameter (mm)/percentage rate (%) | Density (kg m−3) percentage rate (%) | Maximum compressive load (kN)/percentage rate (%) | Compressive strength (MPa)/percentage rate (%) | Compressive strain at maximum compressive load (mm/mm)/percentage rate (%) | Four probe resistivity at maximum compressive loading (kΩ-cm)/percentage rate (%) |
---|---|---|---|---|---|---|
Mo | 225/100 | 2155.6/100 | 93.6/100 | 58.5/100 | 0.0086/100 | 69.8/100 |
GM3 | 213/94.6 | 2045/94.9 | 103.6/110.6 | 64.7/110.6 | 0.012/147.2 | 22.5/32.2 |
GM5 | 211/93.8 | 2150.7/99.8 | 109.2/116.7 | 68.3/116.7 | 0.014/170.1 | 28.3/40.5 |
GM10 | 204/90.7 | 2077.4/96.4 | 95.4/101.9 | 59.6/101.9 | 0.013/153.6 | 35.4/50.8 |