From: Assessment of Rheological and Piezoresistive Properties of Graphene based Cement Composites
Sample | Consistency, K | Power rate index, n | Consistency, K | Power rate index, n |
---|---|---|---|---|
Parallel plate | Concentric cylinders | |||
M0 (control) | 0.60 | 0.96 | 0.59 | 0.82 |
 GM3 | 0.97 | 0.97 | 1.49 | 0.81 |
 GM5 | 0.99 | 0.98 | 1.45 | 0.84 |
 GM10 | 0.97 | 0.98 | 1.53 | 0.83 |
 M0a | 0.29 | 0.60 | 0.89 | 0.74 |
 M0b | 0.60 | 0.96 | 0.58 | 0.82 |
 M0c | 0.51 | 0.90 | 0.76 | 0.74 |
 GM3a | 0.96 | 0.99 | 2.39 | 0.75 |
 GM3b | 0.97 | 0.97 | 1.52 | 0.83 |
 GM3c | 0.96 | 0.98 | 1.49 | 0.81 |
 GM5a | 0.91 | 0.97 | 1.87 | 0.78 |
 GM5b | 0.99 | 0.98 | 1.45 | 0.84 |
 GM5c | 0.98 | 0.94 | 1.67 | 0.80 |
 GM10a | 0.99 | 0.76 | 2.39 | 0.73 |
 GM10b | 0.97 | 0.98 | 1.53 | 0.83 |
 GM10c | 0.99 | 0.86 | 1.52 | 0.81 |
 M0-0 | 0.60 | 0.96 | 0.58 | 0.82 |
 M0-30 | 0.96 | 0.98 | 0.88 | 0.80 |
 M0-60 | 0.22 | 1.21 | 0.47 | 0.72 |
 GM3-0 | 0.97 | 0.97 | 1.52 | 0.83 |
 GM3-30 | 0.92 | 0.99 | 1.88 | 0.82 |
 GM3-60 | 0.99 | 1.10 | 1.94 | 0.83 |
 GM5-0 | 0.99 | 0.98 | 1.45 | 0.84 |
 GM5-30 | 0.97 | 1.03 | 2.03 | 0.81 |
 GM5-60 | 0.92 | 1.01 | 1.73 | 0.80 |
 GM10-0 | 0.97 | 0.98 | 1.53 | 0.83 |
 GM10-30 | 0.99 | 0.99 | 2.08 | 0.80 |
 GM10-60 | 0.13 | 1.20 | 2.71 | 0.77 |
M0 (control) | 0.60 | 0.96 | 0.59 | 0.82 |
 M0S | 0.47 | 0.89 | 0.49 | 0.79 |
 GM3 | 0.97 | 0.97 | 1.49 | 0.81 |
 GM3S | 0.87 | 0.82 | 1.07 | 0.77 |
 GM5 | 0.99 | 0.98 | 1.45 | 0.84 |
 GM5S | 0.67 | 0.82 | 1.19 | 0.83 |
 GM10 | 0.97 | 0.98 | 1.53 | 0.83 |
 GM10S | 0.89 | 0.80 | 0.95 | 0.80 |