From: The Mechanical Properties of Alkali-Activated Slag-Silica Fume Cement Pastes by Mixing Method
 | Age | 10S | 10S-T | 5S5F | 5S5F-T | 5S5F-TA | 5S5F-TB |
---|---|---|---|---|---|---|---|
Total porosity (%) | 1Â day | 36.9 | 34.9 | 33.4 | 33.0 | 31.3 | 31.8 |
28Â days | 35.8 | 33.3 | 33.7 | 32.1 | 31.5 | 30.8 | |
Large capillary pores (10–0.05 µm) (%) | 1 day | 2.12 | 2.16 | 2.43 | 2.36 | 1.95 | 1.79 |
28Â days | 1.98 | 2.35 | 1.94 | 1.53 | 1.79 | 0.88 | |
Medium capillary pores (0.05–0.01 µm) (%) | 1 day | 86.89 | 83.77 | 86.05 | 86.57 | 82.68 | 82.08 |
28Â days | 86.76 | 82.31 | 82.02 | 82.34 | 82.08 | 81.51 | |
Gel pores (≤ 0.01 µm) (%) | 1 day | 10.99 | 14.07 | 11.52 | 11.07 | 15.37 | 16.13 |
28Â days | 11.26 | 15.35 | 16.04 | 16.13 | 16.14 | 17.61 |