From: Study on the Fracture Toughness of Polypropylene–Basalt Fiber-Reinforced Concrete
Specimen | Fiber content (kg/m3) | Compressive strength/MPa | Splitting tensile strength/MPa | |
---|---|---|---|---|
CF | BF | |||
A0 | – | – | 47.13 | 2.65 |
A1 | 6.0 | – | 49.01 | 3.15 |
A2 | 9.0 | – | 48.21 | 3.31 |
A3 | – | 3.0 | 49.06 | 2.68 |
A4 | – | 6.0 | 50.41 | 2.76 |
A5 | 4.8 | 1.2 | 50.93 | 3.21 |
A6 | 4.0 | 2.0 | 53.71 | 3.29 |
A7 | 3.0 | 3.0 | 53.24 | 3.02 |
A8 | 2.0 | 4.0 | 52.58 | 2.94 |
A9 | 1.2 | 4.8 | 51.32 | 2.84 |
A10 | 6.0 | 3.0 | 52.36 | 3.41 |
A11 | 4.5 | 4.5 | 51.25 | 3.24 |
A12 | 3.0 | 6.0 | 50.27 | 3.15 |