From: Bond Behavior Between Steel Fiber Reinforced Polymer (SRP) and Concrete
Specimen ID | Failure mode | \(P_{max}\) (kN) | \({g}_{max}\) (mm) | \({g}_{ult}\) (mm) | ||
---|---|---|---|---|---|---|
 | Avg [CoV] |  | Avg [CoV] | |||
MD_30_1 | Debonding | 7.95 | 6.80 [0.151] | 0.271 | 0.298 | 0.190 [0.311] |
MD_30_2 | Debonding | 5.08 | 0.111 | 0.128 | ||
MD_30_3 | Debonding | 7.64 | 0.188 | 0.188 | ||
MD_30_4 | Debonding | 6.63 | 0.147 | 0.155 | ||
MD_30_5 | Debonding | 6.42 | 0.195 | 0.199 | ||
MD_30_6 | Debonding | 7.10 | 0.160 | 0.169 | ||
MD_60_1 | Debonding | 14.58 | 12.73 [0.106] | 0.493 | 0.493 | 0.426 [0.168] |
MD_60_2 | Debonding | 13.40 | 0.297 | 0.297 | ||
MD_60_3 | Debonding | 10.56 | 0.402 | 0.402 | ||
MD_60_4 | Debonding | 12.26 | 0.377 | 0.380 | ||
MD_60_5 | Debonding | 13.47 | 0.458 | 0.461 | ||
MD_60_6 | Debonding | 13.25 | 0.453 | 0.454 | ||
MD_60_7 | Debonding | 11.62 | 0.493 | 0.496 | ||
MD_90_1 | Debonding | 11.56 | 14.54 [0.177] | 0.452 | 0.466 | 0.534 [0.247] |
MD_90_2 | Debonding | 12.34 | 0.420 | 0.434 | ||
MD_90_3 | Debonding | 12.90 | 0.498 | 0.508 | ||
MD_90_4 | Debonding | 15.63 | 0.752 | 0.752 | ||
MD_90_5 | Debonding | 16.23 | 0.641 | 0.690 | ||
MD_90_6 | Debonding | 18.10 | 0.461 | 0.470 | ||
MD_90_7_D | Debonding | 15.03 | 0.284 | 0.418 | ||
MD_120_1 | Debonding | 14.14 | 15.89 [0.098] | 0.864 | 0.889 | 0.827 [0.083] |
MD_120_2 | Debonding | 14.02 | 0.646 | 0.727 | ||
MD_120_3 | Debonding | 14.44 | 0.707 | 0.895 | ||
MD_120_4 | Debonding | 16.53 | 0.816 | 0.842 | ||
MD_120_5 | Debonding | 16.27 | 0.741 | 0.743 | ||
MD_120_6 | Debonding | 17.00 | 0.765 | 0.877 | ||
MD_120_7 | Debonding | 18.39 | 0.771 | 0.771 | ||
MD_120_8 | Fiber rupture | 22.70 | 1.365 | 1.365 | ||
MD_120_9_D | Debonding | 16.29 | 0.776 | 0.868 | ||
MD_150_1 | Debonding | 16.00 | 15.40 [0.073] | 0.715 | 0.807 | 0.840 [0.114] |
MD_150_2 | Debonding | 14.84 | 0.659 | 0.866 | ||
MD_150_3 | Debonding | 15.49 | 0.675 | 0.863 | ||
MD_150_4 | Debonding | 16.47 | 0.651 | 1.001 | ||
MD_150_5 | Debonding | 16.71 | 0.667 | 0.691 | ||
MD_150_6 | Debonding | 13.44 | 0.556 | 0.873 | ||
MD_150_7 | Debonding | 14.85 | 0.707 | 0.781 | ||
MD_180_1 | Debonding | 14.85 | 16.29 [0.091] | 1.197 | 1.216 | 0.966 [0.218] |
MD_180_2 | Debonding | 16.38 | 0.611 | 0.611 | ||
MD_180_3 | Debonding | 16.46 | 0.999 | 1.041 | ||
MD_180_4 | Debonding | 14.52 | 0.890 | 0.895 | ||
MD_180_5 | Debonding | 16.95 | 1.110 | 1.110 | ||
MD_180_6_D | Debonding | 18.59 | 0.919 | 0.921 | ||
MD_210_1 | Debonding | 12.97 | 16.06 [0.117] | 0.329 | 1.140 | 1.282 [0.179] |
MD_210_2 | Debonding | 15.84 | 1.370 | 1.430 | ||
MD_210_3 | Debonding | 14.85 | 1.109 | 1.133 | ||
MD_210_4 | Debonding | 17.35 | 0.934 | 1.000 | ||
MD_210_5 | Debonding | 15.40 | 1.699 | 1.699 | ||
MD_210_6 | Debonding | 18.41 | 1.023 | 1.289 | ||
MD_210_7_D | Fiber rupture | 24.12 | 1.165 | 1.165 | ||
MD_210_8_D | Debonding | 17.59 | 0.189 | 1.285 | ||
MD_240_1 | Debonding | 15.83 | 16.08 [0.133] | 0.726 | 1.820 | 1.311 [0.321] |
MD_240_2 | Debonding | 15.84 | 1.771 | 1.844 | ||
MD_240_3 | Debonding | 17.98 | 0.842 | 0.842 | ||
MD_240_4 | Debonding | 12.94 | 0.231 | 0.860 | ||
MD_240_5 | Debonding | 13.73 | 1.081 | 1.510 | ||
MD_240_6 | Debonding | 18.17 | 1.208 | 1.209 | ||
MD_240_7_D | Debonding | 18.10 | 0.941 | 1.094 | ||
LD_240_1_D | Fiber rupture | 13.36 | 12.11 [0.103] | 0.341 | 0.341 | 0.412 [0.153] |
LD_240_2_D | Fiber rupture | 12.09 | 0.461 | 0.463 | ||
LD_240_3_D | Fiber rupture | 10.87 | 0.432 | 0.432 | ||
MD_240_1_B | Debonding | 13.86 | 17.32 [0.204] | 0.221 | 1.794 | 1.219 [0.481] |
MD_240_2_B | Debonding | 17.19 | 0.562 | 1.241 | ||
MD_240_3_B | Debonding | 20.91 | 0.621 | 0.622 |