From: Autogenous Shrinkage and Crack Resistance of Carbon Nanotubes Reinforced Cement-Based Materials
Compositions
C3S
C2S
C3A
C4AF
Ignition loss
Content/wt%
49.86
26.87
10.84
9.68
2.57