From: Steel Fiber Orientation Efficiency Factor Model for a Magnetically Treated Cement-Based Composite
Mortar type | Compaction process | Magnetic induction intensity (G) | Magnetic field exposure time (s) | Test specimen label |
---|---|---|---|---|
NM | No | – | – | NM_X |
Yes | – | – | NM_O | |
Yes | 62.66 | 300 | NM_O_0.25MF_1ET | |
Yes | 125.31 | 300 | NM_O_0.5MF_1ET | |
Yes | 250.62 | 75 | NM_O_1MF_0.25ET | |
Yes | 250.62 | 150 | NM_O_1MF_0.5ET | |
Yes | 250.62 | 300 | NM_O_1MF_1ET | |
NSSM | No | – | – | NSSM_X |
Yes | – | – | NSSM_O | |
Yes | 62.66 | 300 | NSSM_O_0.25MF_1ET | |
Yes | 125.31 | 300 | NSSM_O_0.5MF_1ET | |
Yes | 250.62 | 75 | NSSM_O_1MF_0.25ET | |
Yes | 250.62 | 150 | NSSM_O_1MF_0.5ET | |
Yes | 250.62 | 300 | NSSM_O_1MF_1ET | |
SSM | No | – | – | SSM_X |
Yes | – | – | SSM_O | |
Yes | 62.66 | 300 | SSM_O_0.25MF_1ET | |
Yes | 125.31 | 300 | SSM_O_0.5MF_1ET | |
Yes | 250.62 | 75 | SSM_O_1MF_0.25ET | |
Yes | 250.62 | 150 | SSM_O_1MF_0.5ET | |
Yes | 250.62 | 300 | SSM_O_1MF_1ET |