International Journal of Concrete Structures and Materials

Table 9 Magnetic analysis results

From: Steel Fiber Orientation Efficiency Factor Model for a Magnetically Treated Cement-Based Composite

ID	Magnetic analysis model								Mortar type
	Cement		Water		Sand		Steel Slag		NM mortar		NSSM mortar		SSM mortar
	B (T)	H (A/m)	B (T)	H (A/m)	B (T)	H (A/m)	B (T)	H (A/m)	B (T)	µ = B/H (N/A²)	B (T)	µ = B/H (N/A²)	B (T)	µ = B/H (N/A²)
SF01	0.36	171.38	0.36	171.38	0.36	171.38	0.11	73.47	0.36	0.00209	0.30	0.00196	0.25	0.00184
SF02	0.17	107.87	0.17	107.87	0.17	107.87	0.12	76.59	0.17	0.00160	0.16	0.00158	0.15	0.00156
SF03	0.16	98.04	0.16	98.04	0.16	98.04	0.12	79.38	0.16	0.00159	0.15	0.00157	0.14	0.00155
SF04	0.35	162.84	0.35	162.84	0.35	162.84	0.11	73.82	0.35	0.00217	0.30	0.00203	0.25	0.00189
SF05	0.22	131.34	0.22	131.34	0.22	131.34	0.11	75.09	0.22	0.00169	0.20	0.00165	0.18	0.00161
SF06	0.13	84.85	0.13	84.85	0.13	84.85	0.12	79.34	0.13	0.00151	0.13	0.00151	0.12	0.00151
SF07	0.15	98.17	0.15	98.17	0.15	98.17	0.12	78.52	0.15	0.00156	0.15	0.00155	0.14	0.00154
SF08	0.18	101.97	0.18	101.97	0.18	101.97	0.12	77.08	0.18	0.00176	0.17	0.00170	0.15	0.00165
SF09	0.14	93.46	0.14	93.46	0.14	93.46	0.12	82.16	0.14	0.00151	0.14	0.00151	0.13	0.00151
SF10	0.18	119.46	0.18	119.46	0.18	119.46	0.12	80.58	0.18	0.00150	0.17	0.00150	0.15	0.00151
SF11	0.36	159.85	0.36	159.85	0.36	159.85	0.12	80.79	0.36	0.00225	0.31	0.00209	0.26	0.00193
SF12	0.28	165.85	0.28	165.85	0.28	165.85	0.12	79.63	0.28	0.00167	0.24	0.00164	0.21	0.00160
SF13	0.32	168.42	0.32	168.42	0.32	168.42	0.12	80.99	0.32	0.00188	0.27	0.00180	0.23	0.00172
SF14	0.27	157.79	0.27	157.79	0.27	157.79	0.12	79.83	0.27	0.00173	0.24	0.00168	0.21	0.00163
SF15	0.33	178.50	0.33	178.50	0.33	178.50	0.13	87.54	0.33	0.00186	0.29	0.00178	0.25	0.00171
Average									0.24	0.00176	0.21	0.00170	0.19	0.00165

Where B is the magnetic induction intensity, H is the external field, and µ is the permeability